fan gate, is a gate spreading toward in to cavity, basically this gate is thin similarly with previous gate (film gate) and is used in same purpose with film gate. with the gate construction it permits rapid filling of large parts or fragile section mold area with large entry area. it is used to create uniform flow into wide parts.
Purpose
1. thereby keeping the cross sectional area constant.
2. This ensures a constant and more even plastic flow into the cavity into a wide area at a slow injection speed, minimizing backfilling and reducing imperfections and stresses in the part.
3. used for thick-sectioned moldings and enables slow injection without freeze-off.
4. favored for low stress moldings or where warpage and dimensional stability are main concerns.
5.The melt velocity will be constant.
6.The entire width is being used for the flow.
7. The pressure is the same across the entire width
Construction and Design
side View
The gate should taper in both width and thickness, to maintain a constant cross sectional area, although at picture below thickness is doesn't tapered.
Dimension
the land thickness can be vary thin relative to the part thickness because the gate is very wide.the maximum thickness should be no more than 80% of the part thickness. if the parts very thin like 0,8 mm, you can also use 0.7 mm fan gate thickness, but when rubber is used as material parts, use 100 % of the thickness parts is more easy to control flow and product quality. The gate width varies typically from 6 mm up to 25% of the cavity length.in large parts is often use fan gate as wide as the parts it self.
Simulation Picture
all picture below based on injection simulation process, using material PS ASAHIPS 693 : Asahi Chemical
other data are
==== Machine setup ====
Melt temperature = 503.15 K
Mold temperature = 323.15 K
Fill time = 0.08 s
Packing/Holding time = 4.24 s
Cooling time = 7.72 s
Packing/Holding pressure = 12627300.00 Pa
==== Machine specification ====
Required clamp force = 27647.70 N
Required shot size (GPS) = 0.01 kg
Simulation results
mold time filling in seconds
time to cool after injection
from below picture we can learn where is the best position to make cooling layout, after you make cooling layout, enter the cooling simulation process to your parts. if the distribution is same in all shape of part (unless runner and gate) your design is good to realize.
Pressure distribution
Purpose
1. thereby keeping the cross sectional area constant.
2. This ensures a constant and more even plastic flow into the cavity into a wide area at a slow injection speed, minimizing backfilling and reducing imperfections and stresses in the part.
3. used for thick-sectioned moldings and enables slow injection without freeze-off.
4. favored for low stress moldings or where warpage and dimensional stability are main concerns.
5.The melt velocity will be constant.
6.The entire width is being used for the flow.
7. The pressure is the same across the entire width
Construction and Design
side View
The gate should taper in both width and thickness, to maintain a constant cross sectional area, although at picture below thickness is doesn't tapered.
Dimension
the land thickness can be vary thin relative to the part thickness because the gate is very wide.the maximum thickness should be no more than 80% of the part thickness. if the parts very thin like 0,8 mm, you can also use 0.7 mm fan gate thickness, but when rubber is used as material parts, use 100 % of the thickness parts is more easy to control flow and product quality. The gate width varies typically from 6 mm up to 25% of the cavity length.in large parts is often use fan gate as wide as the parts it self.
Simulation Picture
all picture below based on injection simulation process, using material PS ASAHIPS 693 : Asahi Chemical
other data are
==== Machine setup ====
Melt temperature = 503.15 K
Mold temperature = 323.15 K
Fill time = 0.08 s
Packing/Holding time = 4.24 s
Cooling time = 7.72 s
Packing/Holding pressure = 12627300.00 Pa
==== Machine specification ====
Required clamp force = 27647.70 N
Required shot size (GPS) = 0.01 kg
Simulation results
mold time filling in seconds
time to cool after injection
from below picture we can learn where is the best position to make cooling layout, after you make cooling layout, enter the cooling simulation process to your parts. if the distribution is same in all shape of part (unless runner and gate) your design is good to realize.
Pressure distribution
Thanks a lot for sharing this amazing knowledge with us. This site is fantastic. I always find great knowledge from it. Deep Drawing
ReplyDeleteI appreciate your writings. Please look at my articles Castle Hill Dentist Thank you.
ReplyDeleteDisplay Racks in Lahore- TMG Ventures
ReplyDeleteTMG Ventures also deals in Superstore Racks in Lahore. And the various designs of our racks give more attraction to induce customers.
Large varieties of accessories and shelves are available to opt for your business that can add more space that definitely will make your store standout from your competitor.
Even if we supply standard superstore racks in Lahore but these can be customized as per the order or clients needs. Wall shelving unites, single side racks, are among the common forms of superstore racks that we deals in.
display racks in lahore, superstore racks in lahore, garments racks in Lahore
http://www.tmgventures.net/display-racks-in-lahore-superstore-racks-in-lahore-garments-racks-in-lahore/